5 minute epoxy

Manufactured by 3M
Visit Supplier

5 Minute Epoxy is a two-part adhesive product manufactured by 3M. It is designed to quickly bond and seal a variety of materials, including metal, wood, glass, and ceramic. The epoxy sets in approximately 5 minutes, providing a strong and durable bond.

Automatically generated - may contain errors

Lab products found in correlation

Fe no3 3 9h2o, by Merck Group (1 mentions) Carbon felt, by Thermo Fisher Scientific (1 mentions) Cyanamide aqueous solution, by Thermo Fisher Scientific (1 mentions) Cu no3 2 3h2o, by Merck Group (1 mentions)

2 protocols using 5 minute epoxy

1

Iron-Doped Carbon Felt Electrode Synthesis

Check if the same lab product or an alternative is used in the 5 most similar protocols
A precursor solution was first prepared by dissolving 4 g of Fe(NO3)3·9H2O (Sigma-Aldrich) and 0.4 g of PVP (Sigma-Aldrich) into 5.6 mL of deionized water. A piece of carbon felt (Alfa-Aesar) of cross-sectional area 1 cm2 and length 5 cm was treated by O2 plasma for 5 min and then dipped in the precursor solution. 4.5 g of the precursor solution was absorbed by the carbon felt. Excess solution was gently squeezed out. The carbon felt was dried at 60 °C in a vacuum oven overnight. After drying, the carbon felt was put in a tube furnace, heated to 500 °C in 1 h under 1 a.t.m. Ar atmosphere and maintained at this temperature for 1.5 h. The side faces of the carbon felt were then sealed by epoxy (Devcon 5 Minute Epoxy) and wrapped by a piece of duct tape (3M).
Xu J., Zheng X., Feng Z., Lu Z., Zhang Z., Huang W., Li Y., Vuckovic D., Li Y., Dai S., Chen G., Wang K., Wang H., Chen J.K., Mitch W, & Cui Y. (2020). Organic wastewater treatment by a single-atom catalyst and electrolytically produced H2O2. Nature sustainability, 4, 233-241.
+ Open protocol
+ Expand
2

Synthesis of Cu-Decorated Carbon Felt

Check if the same lab product or an alternative is used in the 5 most similar protocols
A precursor solution was first prepared by dissolving 1.436 g of Cu(NO3)2·3H2O (Sigma-Aldrich) into 10 g of 50 wt.% cyanamide aqueous solution (Alfa-Aesar). A piece of carbon felt (Alfa-Aesar) of cross-sectional area 1 cm2 and length 5 cm was treated by O2 plasma for 5 min and then dipped in the precursor solution. 4.5 g of the precursor solution was absorbed by the carbon felt. Excess solution was gently squeezed out. The carbon felt was wrapped by a piece of aluminum foil without drying, and then put in a tube furnace, heated to 550 °C in 40 min under 1 a.t.m. Ar atmosphere and maintained at this temperature for 1 h. The side faces of the carbon felt were then sealed by epoxy (Devcon 5 Minute Epoxy) and wrapped by a piece of duct tape (3M).
Xu J., Zheng X., Feng Z., Lu Z., Zhang Z., Huang W., Li Y., Vuckovic D., Li Y., Dai S., Chen G., Wang K., Wang H., Chen J.K., Mitch W, & Cui Y. (2020). Organic wastewater treatment by a single-atom catalyst and electrolytically produced H2O2. Nature sustainability, 4, 233-241.
+ Open protocol
+ Expand

About PubCompare

Our mission is to provide scientists with the largest repository of trustworthy protocols and intelligent analytical tools, thereby offering them extensive information to design robust protocols aimed at minimizing the risk of failures.

We believe that the most crucial aspect is to grant scientists access to a wide range of reliable sources and new useful tools that surpass human capabilities.

However, we trust in allowing scientists to determine how to construct their own protocols based on this information, as they are the experts in their field.

Ready to get started?

Sign up for free.
Registration takes 20 seconds.
Available from any computer
No download required

Sign up now

Revolutionizing how scientists
search and build protocols!