Example 3
1 g of polymethyl methacrylate (manufactured by Sigma-Aldrich Co. LLC.) was dissolved in 10 mL of toluene, then 10 mg of Compound (3) was added to prepare a coloring agent resin solution which was then spin-coated on a glass plate at 2000 rpm and dried on a hot plate at 50° C. to prepare a wavelength conversion luminescent resin composition (wavelength conversion member) (see paragraph [0081] of JP2011-241160A).
Example 5
A wavelength conversion luminescent resin composition (wavelength conversion member) was prepared in the same manner as in Example 3, except that polymethyl methacrylate was replaced by polyvinyl chloride (manufactured by Sigma-Aldrich Co. LLC.).
Example 7
A wavelength conversion luminescent resin composition (wavelength conversion member) was prepared in the same manner as in Example 3, except that polymethyl methacrylate was replaced by polycarbonate (manufactured by Kanto Chemical Co., Ltd.).
Example 8
A wavelength conversion luminescent resin composition (wavelength conversion member) was prepared in the same manner as in Example 3, except that polymethyl methacrylate was replaced by triacetyl cellulose (manufactured by Wako Pure Chemical Industries, Ltd.), and toluene was replaced by methylene chloride.