Filler 920du40

Example 13

CSBO (100 parts by weight), CA-TETA (72.7 parts by weight, containing 16.86% of carbamate salt, such as 12.2 parts by weight of carbamate salt and 60.5 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO and CA-TETA), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 60 minutes to obtain a product. The product had a density of 80 Kg/m³, a tensile strength of 0.10 Kgf/cm², and an elongation of 94.7%.

Example 20

RDCE (100 parts by weight), CA-TETA (53.6 parts by weight, containing 16.86% of carbamate salt, such as 9.0 parts by weight of carbamate salt and 44.6 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of RDCE and CA-TETA), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of RDCE and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 30 minutes to obtain a product. The product had a density of 138 Kg/m³, a tensile strength of 1.24 Kgf/cm², and an elongation of 9.5%.

Example 14

CSBO (100 parts by weight), CA-TETA (28.8 parts by weight, containing 16.86% of carbamate salt, such as 4.8 parts by weight of carbamate salt and 24.0 parts by weight of TETA), CA-TMD (7.6 parts by weight, containing 14.23 wt % of carbamate salt, such as 1.1 parts by weight of carbamate salt and 6.5 parts by weight of TMD), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CA-TETA, and CA-TMD), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CA-TETA, and CA-TMD) were stirred to mix well, and then put into an oven at 150° C. for 30 minutes to obtain a product. The product had a density of 109 Kg/m³, a tensile strength of 0.31 Kgf/cm², an elongation of 67.2%, and a tear strength of 0.53 Kgf/cm.

Example 21

CSBO (100 parts by weight), CDCE (28.6 parts by weight), CA-TETA (50.3 parts by weight, containing 16.86% of carbamate salt, such as 8.5 parts by weight of carbamate salt and 41.8 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CDCE, and CA-TETA), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CDCE, and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 30 minutes to obtain a product. The product had a density of 94 Kg/m³, a tensile strength of 0.51 Kgf/cm², an elongation of 27.4%, and a tear strength of 0.45 Kgf/cm.

Example 19

PE300C (100 parts by weight), CA-TETA (59.7 parts by weight, containing 16.86% of carbamate salt, such as 10.1 parts by weight of carbamate salt and 49.6 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of PE300C and CA-TETA) and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of PE300C and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 30 minutes to obtain a product. The product had a density of 142 Kg/m³, a tensile strength of 0.88 Kgf/cm², and an elongation of 15.1%.

Example 21

CSBO (100 parts by weight), CDCE (28.6 parts by weight), CA-TETA (50.3 parts by weight, containing 16.86% of carbamate salt, such as 8.5 parts by weight of carbamate salt and 41.8 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CDCE, and CA-TETA), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO, CDCE, and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 30 minutes to obtain a product. The product had a density of 94 Kg/m³, a tensile strength of 0.51 Kgf/cm², an elongation of 27.4%, and a tear strength of 0.45 Kgf/cm.

Example 13

CSBO (100 parts by weight), CA-TETA (72.7 parts by weight, containing 16.86% of carbamate salt, such as 12.2 parts by weight of carbamate salt and 60.5 parts by weight of TETA), filler 031DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO and CA-TETA), and filler 920DU40 (commercially available from AkzoNobel, 2.5% of the total weight of CSBO and CA-TETA) were stirred to mix well, and then put into an oven at 150° C. for 60 minutes to obtain a product. The product had a density of 80 Kg/m³, a tensile strength of 0.10 Kgf/cm², and an elongation of 94.7%.