Exl 101

Example 4

Production of Toner 5

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 73 parts by mass

Polyester resin RN-290 (available from Kao Corporation): 20 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain TOYOTAC-T (available from Toyobo Co., Ltd., having a ½ outflow temperature of 95 degrees C., a weight average molecular weight of 75,000, and a maleic acid modification rate of 1.5% by mass): 2 parts by mass

A toner 5 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 110 degrees C.

Example 3

Production of Toner 4

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 73 parts by mass

Polyester resin RN-290 (available from Kao Corporation): 20 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain TOYOTAC-H3000P (available from Toyobo Co., Ltd., having a ½ outflow temperature of 137 degrees C., a weight average molecular weight of 200,000, and a maleic acid modification rate of 5.5% by mass): 2 parts by mass

A toner 4 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 110 degrees C.

Example 9

Production of Toner 11

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 93 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain TOYOTAC-F7 (available from Toyobo Co., Ltd., having a ½ outflow temperature of 125 degrees C., a weight average molecular weight of 90,000, and a maleic acid modification rate of 1.1% by mass): 2 parts by mass

A toner 11 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 99 degrees C.

Example 11

Production of Toner 13

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 75 parts by mass

Polyester resin RN-290 (available from Kao Corporation): 20 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain TOYOTAC-F7 (available from Toyobo Co., Ltd., having a ½ outflow temperature of 125 degrees C., a weight average molecular weight of 90,000, and a maleic acid modification rate of 1.1% by mass): 0.1 parts by mass

A toner 13 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 114 degrees C.

Example 5

Production of Toner 6

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 73 parts by mass

Polyester resin RN-290 (available from Kao Corporation): 20 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain TOYOTAC-KH (available from Toyobo Co., Ltd., having a ½ outflow temperature of 80 degrees C., a weight average molecular weight of 90,000, and a maleic acid modification rate of 1.1% by mass): 2 parts by mass

A toner 6 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 110 degrees C.

Example 7

Production of Toner 8

Polyester resin EXL-101 (available from Sanyo Chemical Industries, Ltd.): 73 parts by mass

Polyester resin RN-290 (available from Kao Corporation): 20 parts by mass

Ester wax WEP-5 (available from NOF CORPORATION): 5 parts by mass

White pigment (titanium oxide) PF-739 (available from Ishihara Sangyo Kaisha, Ltd.): 65 parts by mass

Maleic-acid-modified polyolefin having a polypropylene block in the main chain

TOYOTAC-TE (available from Toyobo Co., Ltd., having a ½ outflow temperature of 95 degrees C., a weight average molecular weight of 60,000, and a maleic acid modification rate of 2.0% by mass): 2 parts by mass

A toner 8 was manufactured in the same manner as the toner 1 except that the toner raw materials were replaced with the materials listed above. The ½ outflow temperature of the toner was 110 degrees C.