Ultrasonic processor up 400s

The Fe₂O₃-UF nanofluid was primed in the Institute of Space Technology, Islamabad, Pakistan materials Science Work room according to the configurations specified in Table 3.
The nanofluids were blended by weighing 200 g of urea-formaldehyde resin and 0, 1.3 and 5 g of iron oxide (Fe₂O₃) nanoparticles of dry weight of fibers. The sonication of the nanofluids was carried out by means of Ultrasonic Processor UP 400S of Hielscher Ultrasound Technology Company, USA for 30 min. The samples were signified by Fe₀, Fe₁, Fe₂ and Fe₃ rendering to the meditation of Fe₂O₃. The iron oxide (Fe₂O₃) nanoparticles, urea-formaldehyde resin, poplar wood fibers, nanofillers, sonication and curing of the fillers can be seen in Figure 2.

The MWCNTs-UF nanofluid was primed in the materials Science Lab, Institute of Space Technology, Islamabad, Pakistan with the configurations specified in Table 2 dignified in grams.
The nanofluids were blended by weighing 200 g of urea-formaldehyde resin and 0, 1.5, 3 and 5 wt% of MWCNTs of dry weight of fibers. The sonication of the nanofluids was carried out by means of an Ultrasonic Processor UP 400S of Hielscher Ultrasound Technology Company, USA, for 30 min. The samples were signified by MWCNTs₀, MWCNTs₁, MWCNTs₂ and MWCNTs₃,according to the meditation of MWCNTs.